Structures by: Miller D. J.
Total: 7
Zn21.8 Mg6.6 Y7.6
Mg6.6Y7.6Zn21.8
Journal of Alloys Compd. (2004) 373, 156-160
a=9.0822Å b=9.0822Å c=9.4155Å
α=90° β=90° γ=120°
C36H36CuN8O3S
C36H36CuN8O3S
Journal of the Chemical Society, Dalton Transactions (2002) 22 4128
a=11.3898(15)Å b=14.843(2)Å c=40.196(5)Å
α=90.00° β=95.298(2)° γ=90.00°
C36H34CuN8O2
C36H34CuN8O2
Journal of the Chemical Society, Dalton Transactions (2002) 22 4128
a=13.184(3)Å b=27.498(7)Å c=19.121(5)Å
α=90.00° β=108.662(4)° γ=90.00°
C40H46CuN8O4S2
C40H46CuN8O4S2
Journal of the Chemical Society, Dalton Transactions (2002) 22 4128
a=11.592(5)Å b=16.662(5)Å c=10.435(5)Å
α=93.233(5)° β=94.704(5)° γ=99.777(5)°
C28H19N5S2
C28H19N5S2
Journal of the American Chemical Society (2012) 134, 13616-13623
a=7.6787(2)Å b=16.9340(4)Å c=18.3591(4)Å
α=90.00° β=92.984(2)° γ=90.00°
C30H21N5S
C30H21N5S
Journal of the American Chemical Society (2012) 134, 13616-13623
a=8.9955(4)Å b=13.0986(6)Å c=20.8888(9)Å
α=90.000° β=93.997(4)° γ=90.000°
Mg1.44O24Sc2.56Si8,1.44(Ca),2.56(Na)
Mg1.44O24Sc2.56Si8,1.44(Ca),2.56(Na)
Journal of the American Chemical Society (2016) 138, 4 1158-1161
a=9.8048(12)Å b=9.0206(10)Å c=5.31486(65)Å
α=90° β=106.5441(43)° γ=90°